Monolithic
Formulations for Ferrous Casting Foundry Industry
|
|
| Casting
Foundries melting Alloy Steel, Carbon Steel, Stainless Steel and Manganese Steel
normally use Induction Furnaces. We manufacture a range of products based on Magnesite
for lining of these furnaces. All these products are manufactured at the plant
located at Rabale in New Mumbai. The table below gives the detailed specifications |
|
| INDSPINEL
A | INDSPINEL
C |
INDPATCH
| INDKOTE | INDTOP |
MgO | 70%
Min. | 70%
Min. | 70%
Min. | 80%
Min | 70%
Min |
SiO2
| 8%
Max. | 8%
Max. | 8%
Max. | 8%
Max. | 8%
Max. |
Al2O3
| 20
% Min. | - | - | - | - |
Cr2O3
| - | 8%
Max. | 8%
Max. | - | 8%
Min |
Setting | Chemical/
Heat | Chemical/
Heat | Hydraulic/
Heat | Hydraulic/
Heat | Hydraulic/
Heat |
Grading | 0-5
mm | 0-5
mm | 0
to 1 mm | 0-0.25
mm | 0-5
mm |
Packing | 50
Kg. | 50
Kg. | 50
Kg. | 50
Kg. | 50
Kg. |
Use |
Special
Alloy Steels | For
all qualities of steel especially foundries with interrupted operations. | All
Purpose | For
coil coating | For
making the mouth Top of the induction furnace above coil level |
|
| Indspinel
A & C An
Induction furnace ramming material made from Dead Burnt Magnesite clinker in association
with either Alumina or Chrome. Specially bonded with clays and other chemical
binders to achieve the desired sintering characteristics.
|
|
Indpatch
This material is designed
for repairing the cracks and other erosion that occurs in the lining during usage.
It possesses good workability and has no shrinkage upto 1650 0 C and has good
erosion resisting properties. The chemical composition is similar to the ramming
mass but the grading/ binder is different for good workability. |
|
Indkote
This
is a High MgO based refractory powder blended with suitable binders to protect
the Induction furnace coils. |
|
Indtop
MgO
based formulation to be used with 8 to 10 % foundry grade Sodium Silicate for
making the area of furnace outside the coil and mouth of furnace. Product has
good resistance to wear due to mechanical abrasion. |